Stainless Steel Grades: The Ultimate Guide

Have you ever wondered about the different types of stainless steel and their applications? In this blog post, we’ll dive into the world of stainless steel grades, exploring their unique characteristics and uses. Our expert mechanical engineer will guide you through the complexities, providing insights to help you select the perfect grade for your needs. Get ready to expand your knowledge and discover the fascinating world of stainless steel!

Stainless Steel Grades

Table Of Contents

The following information will provide you with a comprehensive understanding of the different grades of stainless steel, making it easier for you to choose the appropriate type for your needs.

Presently, the most widely used stainless steels are 304 and 316.

In terms of cost, 304 stainless steel is significantly less expensive than 316 stainless steel.

You can select the appropriate type of stainless steel based on your specific requirements.

Stainless Steel Grades

Stainless Steel Grades

This following table summarizes the different series of stainless steel and their specific types, along with their key characteristics and typical applications.

SeriesStainless Steel TypeCharacteristics and Applications
200GeneralContains chrome, nickel, manganese; austenitic stainless steel.
300GeneralContains chrome, nickel; austenitic stainless steel.
301SpecificGood malleability, quickly hardened, good weldability, superior abrasion resistance and fatigue strength to 304.
302SpecificSame corrosion resistance as 304, higher strength due to high carbon content.
303SpecificEasier machining than 304, small amounts of sulfur and phosphorus added.
304SpecificGeneral model, 18/8 stainless steel, GB grade 0Cr18Ni9.
309SpecificBetter temperature resistance than 304.
316SpecificUsed in food industry and surgical equipment, anti-corrosive, better anti-chloride corrosion resistance, “Marine steel”, used in nuclear fuel recovery.
321SpecificReduced corrosion risk at weld joints due to titanium, similar to 304.
400GeneralFerritic and martensitic stainless steel.
408SpecificGood heat resistance, weak corrosion resistance, 11% Cr, 8% Ni.
409SpecificCheap, used as car exhaust pipe, ferritic (chrome steel).
410SpecificMartensitic (high-strength chromium steel), good wear resistance, poor corrosion resistance.
416SpecificImproved processing properties due to added sulfur.
420Specific“Blade grade” martensitic steel, used for surgical tools, very bright.
430SpecificFerritic, decorative use, good forming property, poor temperature endurance and corrosion resistance.
440SpecificUsed for razor blades, models: 440A, 440B, 440C, 440F (easily processed).
500GeneralHeat-resistant chromium alloy steel.
600GeneralMartensite precipitation hardening stainless steel.
630SpecificCommon precipitation hardened type, 17-4; 17% Cr, 4% Ni.

Stainless Steel Classification

The main chemical composition of stainless steel can be divided into several categories, including chromium stainless steel, chromium-nickel stainless steel, chromium-manganese-nitrogen stainless steel, chromium-nickel-molybdenum stainless steel, ultra-low carbon stainless steel, high molybdenum stainless steel, and high-purity stainless steel.

Classification based on steel properties and application includes nitric acid (nitric grade) stainless steel, corrosion-resistant stainless steel, stress stainless steel, high-strength stainless steel, among others.

In terms of functional characteristics, stainless steel can be divided into low-temperature stainless steel, non-magnetic stainless steel, easy-cutting stainless steel, and ultra-plastic stainless steel.

It is also classified based on its metallographic structure, which includes ferrite (F) stainless steel, martensite stainless steel (M), austenitic stainless steel, austenitic-ferritic duplex stainless steel (A-F), austenite-martensite duplex stainless steel (A-M), and precipitation-hardening stainless steel (PH).

Stainless Steel Mechanical Properties

Comparison of mechanical properties of stainless steel

ClassificationComposition (%)HardenabilityCorrosion-resistanceMachinabilityWeldabilityMagnetism

The above classification only considers the matrix structure.

In addition to the three basic types of stainless steel, it also includes composite stainless steel, such as martensite-ferrite and austenite-ferrite, as well as precipitation-hardening stainless steel, such as martensite-carbide stainless steel.

Detailed Introduction to Stainless Steel

This table below provides a concise overview of each type of steel, highlighting their main features, examples, and typical applications.

Type of S.SKey CharacteristicsExamplesUses
Ferritic Steel– Low-carbon chromium stainless steel.
– Chromium content > 14%.
– Contains elements like Mo, Ti, Nb, Si, Al, W, V.
– Dominantly ferrite-forming elements.
– Corrosion-resistant and oxidation-resistant.
– Poor mechanical properties and processability.
Cr17, Cr17Mo2Ti, Cr25, Cr25Mo3Ti, Cr28Anti-acid structures, antioxidant steel.
Ferrite-Martensitic Steel– In Y+A or δ phase at high temperatures.
– Transforms to Y-M phase in cold conditions.
– Consists of ferrite and martensite.
– Ferrite amount varies.
– Chromium content typically between 12-18%.
– Partial hardening possible.
0Cr13, 1Cr13, 2Cr13, Cr17Ni2, Cr17W4, Cr11MoV, etc.Various applications, depends on specific grade.
Martensitic Steel– In Y phase at quenching temperatures.
– Transforms into martensite upon cooling.
– Similar properties to ferritic-martensitic steel but higher mechanical performance.
– No free ferrite in the structure.
2Cr13, 2Cr13Ni2, 3Cr13, 13Cr14NiWVBA, etc.Various applications similar to ferritic-martensitic steel.
Martensite-Carbide Steel– High carbon content Fe-C alloy.
– Contains 12% or more chromium.
– Heated at normal quenching temperature.
– Hardened structure of martensite and carbide.
– Corrosion resistance equivalent to 12-14% chromium stainless steel.
4Cr13, 9Cr18, 9Cr18MoV, 9Cr17MoVCoCutting tools, bearings, springs, medical instruments.
Austenitic Steel– High concentration of stabilizing elements.
– Broad Y-phase zone at high temperatures.
– Austenitic structure at normal temperatures.
– Can be strengthened by cold deformation.
– Susceptible to intercrystalline and stress corrosion.
18-8, 18-12, 25-20, 20-25Mo, Cr18Mn10Ni5, etc.Various industrial applications, benefits from strain hardening.
Austenitic-Ferritic Steel– Limited stable austenite elements.
– Austenitic-ferritic phase state.
– Composition and amount of ferrite varies.
– Higher yield strength compared to pure austenitic steel.
– Less susceptible to stress corrosion and hot cracking during welding.
– Poor pressure processing performance and high susceptibility to pitting corrosion.
Various chromium-manganese stainless steelsIndustries requiring high yield strength and corrosion resistance.
Austenite-Martensitic Steel– Ms point lower than room temperature.
– Forms austenite after solid solution treatment.
– Transforms to martensite during cooling or heating processes.
– High strength but lower corrosion resistance than standard austenitic steel.
– Developed in the 1950s, known as half austenitic precipitation-hardening stainless steel.
17Cr-7Ni-A1, 15Cr-9Ni-A1, 17Cr-5Ni-Mo, etc.Aviation, rocket missile industries; not widely used in machinery manufacturing. Ultra-high strength steel.

1. Ferritic steel

Low-carbon chromium stainless steel with a chromium content of more than 14%, chromium stainless steel with a chromium content of 27% and above, and with additional elements such as molybdenum, titanium, niobium, silicon, aluminum, tungsten, and vanadium.

In the chemical composition, elements that form ferrite hold a dominant position, and the matrix structure is primarily iron-based.

This type of steel is known as ferritic, with a quenched (solid solution) form, and small amounts of carbide and intermetallic compounds can be observed in the structures of annealing and aging.

Examples of such steels include Cr17, Cr17Mo2Ti, Cr25, Cr25Mo3Ti, and Cr28.

Ferritic stainless steel is relatively corrosion-resistant and oxidation-resistant due to its high chromium content, but it has poor mechanical properties and processability.

It is mostly used in anti-acid structures and as an antioxidant steel.

2. Ferrite-martensitic steel

This type of steel is in the Y+A (or δ) phase at high temperatures, and transforms to the Y-M phase when it approaches cold conditions.

It retains ferrite and exists as martensite and ferrite at normal temperatures.

The amount of ferrite in the structure can vary from a few percent to several tens percent, depending on the composition and heating temperature.

Examples of this type of steel include 0Cr13, 1Cr13, 2Cr13 with chromium near the upper limit and carbon near the lower limit, Cr17Ni2 steel, Cr17W4 steel, as well as many modified 12% chromium hot-strength steels based on 1Cr13 (which are also known as heat-resistant stainless steels), such as Cr11MoV, Cr12WMoV, Cr12W4MoV, 18Cr12WMoVNb, etc.

Ferritic-martensitic steel can exhibit partial hardening and obtain mechanical properties, but these are greatly influenced by the content and distribution of ferrite.

The chromium content in this type of steel is typically between 12-14% and 15-18%.

The former has the ability to resist atmospheric and weak corrosive media, and has good damping and a small linear expansion coefficient.

The latter type has comparable corrosion resistance to ferritic acid steel with the same chromium content, but still retains some of the disadvantages of high chromium ferritic steel.

3. Martensitic steel

Under normal quenching temperatures, martensitic steel is in the Y phase, but this phase only remains stable at high temperatures. The M phase is commonly stable around 300℃ and transforms into martensite upon cooling.

This type of steel includes 2Cr13, 2Cr13Ni2, 3Cr13, and some modified 12% chromium hot-strengthened steel, such as 13Cr14NiWVBA and Cr11Ni2MoWVB steel.

The mechanical properties, corrosion resistance, process performance, and physical properties of martensitic stainless steel are similar to those of 2-14% chromium ferrite-martensitic stainless steel.

Because there is no free ferrite in the structure, its mechanical performance is higher than the aforementioned steel, but its thermal sensitivity to heat treatment is lower.

4. Martensite-carbide steel

Fe-C alloy contains 0.83% carbon.

In stainless steel, the S points are shifted to the left due to chromium. Steel with 12% chromium and 0.4% or more carbon, as well as steel with 18% chromium and 0.3% or more carbon, belong to hypereutectoid steel.

This type of steel is heated at normal quenching temperature, and the secondary carbide cannot be completely dissolved in austenite, so the hardened structure is composed of martensite and carbide.

There are not many grades of stainless steel that fall into this category, but some stainless steels with higher carbon, such as 4Cr13, 9Cr18, 9Cr18MoV, and 9Cr17MoVCo steel.

If quenched under low temperature, the 3Cr13 steel with carbon close to the upper limit may also have such a structure.

Due to its high carbon content, even though the above three grades of steel contain more chromium, their corrosion resistance is only equivalent to that of stainless steel with 12-14% chromium.

This type of steel is mainly used for parts that require high hardness and good wear resistance, such as cutting tools, bearings, springs, and medical instruments.

5. Austenitic steel

This type of steel has a high concentration of stabilizing elements and a broad Y-phase zone at high temperatures.

Upon cooling, the Ms point falls below room temperature, resulting in an austenitic structure at normal temperatures.

This category includes chrome-nickel stainless steel such as 18-8, 18-12, 25-20, and 20-25Mo, as well as low-nickel stainless steel that uses manganese instead of some nickel and nitrogen, including Cr18Mn10Ni5, Cr13Ni4Mn9, Cr17Ni4Mn9N, and Cr14Ni3Mn14Ti steel.

Austenitic stainless steel has many benefits, including the ability to be strengthened by cold deformation methods through strain hardening, despite poor heat treatment properties.

However, it is also susceptible to intercrystalline corrosion and stress corrosion, which can be mitigated through the use of alloy additives and process measures.

6. Austenitic-ferritic steel

Due to the limited amount of stable austenite elements, the steel does not have a pure austenitic structure at room temperature or high temperatures, resulting in an austenitic-ferritic phase state. The composition and amount of ferrite can vary greatly depending on heating temperature.

Many types of stainless steel fall into this category, including low-carbon 18-8 nickel-chrome steel, 18-8 nickel-chrome steel with titanium, niobium, and molybdenum, with ferrite being particularly visible in the structure of cast steel.

Other examples include chromium-manganese stainless steel with more than 14-15% chromium and less than 0.2% carbon (such as Cr17Mn11) and most of the chromium-manganese-nitrogen stainless steel that have been studied and applied in industry.

Compared to pure austenitic stainless steel, this type of steel has several advantages, including higher yield strength, increased resistance to intergranular corrosion, reduced sensitivity to stress corrosion, lower tendency for hot cracking during welding, and good casting fluidity.

However, it also has several disadvantages, such as poor pressure processing performance, high susceptibility to pitting corrosion, and tendency to exhibit c-phase brittleness and weak magnetism under strong magnetic field conditions.

These advantages and disadvantages are directly related to the presence of ferrite in the structure.

7. Austenite-martensitic steel

The Ms point of this steel is lower than room temperature, making it easy to form and weld for austenite after solid solution treatment.

Martensitic transformation can usually be achieved through two processes.

  • After the solid solution treatment, heating at 700-800℃ causes the austenitic body to transform into a metastable state due to the precipitation of carbonized chromium. The Ms point then rises above room temperature, resulting in the transformation of the austenite into martensite during the cooling process.
  • Direct cooling between the Ms and Mf points after the solid solution treatment results in the transformation of the austenite into martensite as well.

The second method provides better corrosion resistance, but the solid solution treatment and cryogenic interval time must not be too long, otherwise, the cold strengthening effect will be reduced due to the aging stability of the austenite.

After the treatment, an aging process at 400-500 degrees is performed to enhance the intermetallic compound.

Examples of steel grades that fall into this category include 17Cr-7Ni-A1, 15Cr-9Ni-A1, 17Cr-5Ni-Mo, and 15Cr-8Ni-Mo-A1.

Austenite-martensitic steel, also known as austenitic-maraging stainless steel, is a new type of stainless steel developed and applied starting in the 1950s.

It is also referred to as half austenitic precipitation-hardening stainless steel due to the presence of ferrite in addition to austenite and martensite in its structure.

These steels are characterized by their high strength (C can reach 100-150) and good heat strengthening performance, but their corrosion resistance is lower than that of standard austenitic stainless steel due to the low chromium content and chromium carbide precipitation during heat treatment.

The high strength is obtained by sacrificing some of the corrosion resistance and other properties, such as non-magnetism.

Austenite-martensitic steel is primarily used in the aviation and rocket missile industries, but is not widely used in machinery manufacturing and is sometimes classified as a type of ultra-high strength steel.

Don't forget, sharing is caring! : )


Founder of MachineMFG

As the founder of MachineMFG, I have dedicated over a decade of my career to the metalworking industry. My extensive experience has allowed me to become an expert in the fields of sheet metal fabrication, machining, mechanical engineering, and machine tools for metals. I am constantly thinking, reading, and writing about these subjects, constantly striving to stay at the forefront of my field. Let my knowledge and expertise be an asset to your business.

Up Next

H Beam Sizes and Weight Chart

Have you ever wondered about the hidden world of H-beam steel? In this captivating article, we'll unravel the mysteries behind these essential construction components. Our expert mechanical engineer will guide…
Take your business to the next level
Subscribe to our newsletter
The latest news, articles, and resources, sent to your inbox weekly.
© 2024. All rights reserved.

Contact Us

You will get our reply within 24 hours.